Electro Galvanized Steel Wire For armoured Size：0.15-1.0mm Tensile Strength：320-500 Mpa Packing： Spool STRENGTH, TENSILE STRENGTH RANGE Specifications (mm) the intensity of the size range (mpa), tensile strength 0.24 -- 1.60:290-550 1.61 -- 5.00:400-1200 ...Send Inquiry
Electro Galvanized Steel Wire is obtained from an external power source and consists of fine, pure zinc grains. When the galvanized steel wire is spirally wound around the core rod having a diameter of 5 times or 10 times the diameter of the steel wire, the zinc layer should not fall off or crack. Corrosion resistance of the galvanized layer should also be repaired accordingly. To ensure the quality of Electro Galvanized Steel Wire, the galvanized steel wire should be smooth, complete, average and firm. Hot-dip galvanizing will reduce the mechanical properties of steel wire, and require high-strength and high-corrosion-resistant galvanized steel wire rope, which is mostly made of electro-galvanized steel wire.
Electro Galvanized Steel Wire For armoured
Tensile Strength：320-500 Mpa
STRENGTH, TENSILE STRENGTH RANGE
Specifications (mm) the intensity of the size range (mpa), tensile strength
0.24 -- 1.60:290-550
1.61 -- 5.00:400-1200
Cold galvanizing, also called electro-galvanizing, is the gradual plating of zinc on the metal surface in the electroplating tank. The production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 microns, and the appearance is bright, smooth and beautiful. High degree, poor corrosion resistance, it will rust in a few months.